婷婷爱爱 I 亚洲中文无码av永久 I a级毛片在线免费 I 日韩avav I 78m78成人免费网站 I 亚洲国产成人精品av区按摩 I 日本黄色a v I 91n.com在线观看 I 99久精品视频 I 歪歪爽蜜臀av久久精品人人 I 国产精品少妇在线视频 I 亚洲欧美日韩中文字幕在线一区 I 欧美精品1区2区 I 操日本美女b I 91精品国产99久久久久 I 国产在线无码视频一区二区三区 I 999久久久免费精品播放 I 天天插综合网 I 亚州视频在线 I 性开放网站 I 午夜在线视频 I 欧美性导航 I 九九热最新地址 I 伊人婷婷久久 I 成人精品中文字幕 I 人妻少妇精品久久久久久 I 中文字幕日日骚 I 欧洲激情一区二区 I 精品亚洲一区二区三区四区 I 很色很爽很黄裸乳视频 I 免费a黄色 I 亚洲欧美文学 I 国产尻逼视频 I 欧美日韩中国免费专区在线看 I 五月天久久网站

To whom it may concern:

The purpose of this memorandum is to discuss some of the sources of variation in anodizing response of aluminum plate products.  Anodizing can be influenced by local variations in composition, precipitate distribution, and grain structure that develop naturally during fabrication.

這個(gè)文件的目的是討論鋁板陽(yáng)極氧化現(xiàn)象變化的來(lái)源。在制造過(guò)程中，陽(yáng)極氧化自然會(huì)受到局部成分變化，沉淀的分布，和晶粒結(jié)構(gòu)的影響。

· 

Aluminum wrought plate is fabricated from thick, direct chill cast ingot.  During the solidification process, solute elements (in the case of 7075, predominantly Zn, Cu, and Mg) are pushed out of the initial metal to solidify and into the remaining liquid, which results in a composition gradient through the thickness (and across the width) of the ingot.  This gradient persists through fabrication, and influences the subsequent formation of precipitates, such that the final plate will have differences in composition and precipitation throughout.

 鋁鍛板是直接由厚，冷硬鑄塊鍛造的。在凝固過(guò)程中，溶質(zhì)元素（在7075的情況下，主要是鋅，銅，鎂）從原材料金屬凝固到剩余的液體，結(jié)果導(dǎo)致鑄塊合成物在厚度和寬度方向有個(gè)梯度變化和分布。這種梯度變化在制造過(guò)程中一直存在，而且影響后面形成的沉淀物，正因?yàn)槿绱俗罱K凝固的板材在構(gòu)造和沉淀物上都有差異。 

· 

Another factor is that grain structure within the plate also varies through the plate thickness and across the width.  These gradients are due in part to composition differences (in this case, the dispersoid former, Cr, is the important element) and in part due to the thermomechanical processing to which the plate is subjected during hot rolling.  As gauge decreases, temperature control is more difficult to maintain, and gradients in grain structure may become more pronounced.

另一個(gè)因素是，板材內(nèi)在的晶粒結(jié)構(gòu)會(huì)隨著厚度和寬度發(fā)生變化。這些梯度變化由于部分構(gòu)造不同而產(chǎn)生（在這種情況下，最先析出的元素，鉻是主要的影響因素），部分原因是由于熱軋過(guò)程中的熱處理產(chǎn)生的。隨著尺寸減小，溫度控制更難以保持，晶粒結(jié)構(gòu)的梯度變化也會(huì)更加明顯。

· 

Finally, when aluminum plate products are quenched after solution heat treatment, the quenching medium (generally water) impinges on the metal surface, efficiently removing heat.  In the interior of the plate, heat must be transferred outward to the surface, resulting in a through thickness gradient in quench rate.  This gradient in quench rate also contributes to local variations in precipitate distribution and anodizing response.
最后，當(dāng)鋁板產(chǎn)品從固溶熱處理中冷卻出來(lái)，淬火介質(zhì)（通常是水）噴淋在金屬表面上，

有效地去除熱降溫。在板的內(nèi)部，熱量必須向外傳遞到表面，導(dǎo)致在一個(gè)通過(guò)厚度梯度的淬火速率。這個(gè)淬火速率的梯度也會(huì)影響晶體的成長(zhǎng)、沉淀的分布和陽(yáng)極氧化反應(yīng)。

· 
Given the gradients discussed above, it is not unusual to have different parts from within the same lot respond differently to anodizing, depending on their location within the lot.

鑒于上述梯度的討論，陽(yáng)極電鍍時(shí)，不同一個(gè)點(diǎn)有不同成分是常見(jiàn)的，這取決于它們?cè)谶@個(gè)點(diǎn)所處的位置。

· 

Because it is a natural outcome of the manufacturing process, anodizing performance in plate is not guaranteed, although Kaiser Aluminum has done a great deal of research over the past several years in an effort to minimize through-thickness differences in anodizing behavior.  This research has culminated in the recent introduction of Kaiser Select^? 6061-T651 plate, offering improved uniformity in through-thickness anodizing response.

因?yàn)?/span>這是制造過(guò)程中的自然結(jié)果，陽(yáng)極氧化板材的性能不能保證，盡管Kaiser鋁業(yè)在過(guò)去幾年里盡量減少厚度差異對(duì)陽(yáng)極電鍍反應(yīng)的影響進(jìn)行了大量研究。本研究最終成果在Kaiser 6061-T651板最近推出，通過(guò)不同厚度的陽(yáng)極氧化反應(yīng)，改進(jìn)板材的均勻性。

· 

Brian A. Cheney

Senior Staff Product Engineer

Kaiser Aluminum – Trentwood Works